Array ( [0] => Array ( [id] => 471 [topology] => kfi [link_rcsr] => http://rcsr.net/nets/kfi [in_col] => 1 [transitivity] => [1453] [space_group] => Im-3m [pearson] => cI96 [cn] => 4 [Year] => 2011 [cn_sort] => 004- [topology_str] => kfi [sp_atoms] => [caid] => 85 [nn] => 0 [name] => [pressure] => [density] => 2.426 [e_gap] => [energy] => 0.851 [bulk_mod] => 255.1 [shear_mod] => 166.6 [vicker_hard] => 18.9 [ref_file] => [publ_year] => [ref] => ) [1] => Array ( [id] => 472 [topology] => kfi [link_rcsr] => http://rcsr.net/nets/kfi [in_col] => 1 [transitivity] => [1453] [space_group] => Im-3m [pearson] => cI96 [cn] => 4 [Year] => 2011 [cn_sort] => 004- [topology_str] => kfi [sp_atoms] => [caid] => 85 [nn] => 1 [name] => CA8 [pressure] => [density] => [e_gap] => [energy] => [bulk_mod] => [shear_mod] => [vicker_hard] => [ref_file] => /References/2011_Journal of Experimental and Theoretical Physics_113_1_ 86 [publ_year] => 2011 [ref] => ) [2] => Array ( [id] => 473 [topology] => kfi [link_rcsr] => http://rcsr.net/nets/kfi [in_col] => 1 [transitivity] => [1453] [space_group] => Im-3m [pearson] => cI96 [cn] => 4 [Year] => 2011 [cn_sort] => 004- [topology_str] => kfi [sp_atoms] => [caid] => 85 [nn] => 2 [name] => CA8 [pressure] => [density] => [e_gap] => [energy] => [bulk_mod] => [shear_mod] => [vicker_hard] => [ref_file] => /References/book_Crystal structures and properties of diamond-like phases of carbon [publ_year] => [ref] => ) )
SACADA Database Code: 85 Topology: kfi ![]() # of independent nodes (IN): 1 Transitivity: [1453] Space Group: Im-3m Pearson: cI96 Coordination Number (CN): 4 Year: 2011 ![]() ![]() |
|
Name |
Pressure, GPa |
Density, g/cm³ |
Gap, eV |
Relative energy, eV/atom |
Bulk, GPa |
Shear, GPa |
Vickers, GPa |
Refs |
---|---|---|---|---|---|---|---|---|
kfi (SACADA #85) | 2.426 | 0.851 | 255.1 | 166.6 | 18.9 | SACADA¹ | ||
CA8 | doi: 10.1134/s1063776111060173 ![]() |
|||||||
CA8 | link ![]() |
5672.2519 | 990.0231 | 994.6088 | 13.1842 | -7.6882 | -1.7732 |
990.0231 | 5666.2550 | 995.1057 | 0.5737 | 12.4424 | -5.2159 |
994.6088 | 995.1057 | 5663.1635 | -5.3874 | -0.2053 | 8.3086 |
13.1842 | 0.5737 | -5.3874 | 1326.2739 | -0.7792 | 1.0191 |
-7.6882 | 12.4424 | -0.2053 | -0.7792 | 1324.3293 | 1.1951 |
-1.7732 | -5.2159 | 8.3086 | 1.0191 | 1.1951 | 1324.0564 |