Array ( [0] => Array ( [id] => 1941 [topology] => 4<sup>4</sup>T24-CA [link_rcsr] => [in_col] => 4 [transitivity] => [4(12)(12)5] [space_group] => Pccn [pearson] => oP32 [cn] => 4 [Year] => 2023 [cn_sort] => 004- [topology_str] => 4^4T24-CA [sp_atoms] => [caid] => 659 [nn] => 0 [name] => [pressure] => [density] => 3.515 [e_gap] => [energy] => 0.295 [bulk_mod] => 432.5 [shear_mod] => 501.2 [vicker_hard] => 94.6 [ref_file] => [publ_year] => [ref] => ) [1] => Array ( [id] => 1942 [topology] => 4<sup>4</sup>T24-CA [link_rcsr] => [in_col] => 4 [transitivity] => [4(12)(12)5] [space_group] => Pccn [pearson] => oP32 [cn] => 4 [Year] => 2023 [cn_sort] => 004- [topology_str] => 4^4T24-CA [sp_atoms] => [caid] => 659 [nn] => 1 [name] => 4<sup>4</sup>T24-CA [pressure] => [density] => [e_gap] => [energy] => [bulk_mod] => [shear_mod] => [vicker_hard] => [ref_file] => /References/2023_ActaCrystB_79 [publ_year] => 2023 [ref] => doi: <a href="http://doi.org/10.1107/S205252062300255X" target="_blank">10.1107/S205252062300255X</a> ) )
SACADA Database Code: 659 Topology: 44T24-CA # of independent nodes (IN): 4 Transitivity: [4(12)(12)5] Space Group: Pccn Pearson: oP32 Coordination Number (CN): 4 Year: 2023 ![]() ![]() |
|
Name |
Pressure, GPa |
Density, g/cm³ |
Gap, eV |
Relative energy, eV/atom |
Bulk, GPa |
Shear, GPa |
Vickers, GPa |
Refs |
---|---|---|---|---|---|---|---|---|
44T24-CA (SACADA #659) | 3.515 | 0.295 | 432.5 | 501.2 | 94.6 | SACADA¹ | ||
44T24-CA | doi: 10.1107/S205252062300255X ![]() |
11447.8275 | 684.9897 | 1204.3116 | 0.0000 | -0.0000 | -0.0000 |
684.9897 | 12046.8075 | 204.3228 | -0.0000 | 0.0000 | 0.0000 |
1204.3116 | 204.3228 | 11251.0534 | 0.0000 | 0.0000 | -0.0000 |
0.0000 | -0.0000 | 0.0000 | 5078.8112 | 0.0000 | -0.0000 |
-0.0000 | -0.0000 | 0.0000 | 0.0000 | 4220.4308 | 0.0000 |
-0.0000 | 0.0000 | -0.0000 | -0.0000 | 0.0000 | 5013.2176 |