Array ( [0] => Array ( [id] => 385 [topology] => crb [link_rcsr] => [in_col] => 1 [transitivity] => [1232] [space_group] => I4/mmm [pearson] => tI24 [cn] => 2, 4 (2:1) [Year] => 2013 [cn_sort] => 002-004-002-001- [topology_str] => crb [sp_atoms] => + [caid] => 61 [nn] => 0 [name] => [pressure] => [density] => 1.911 [e_gap] => [energy] => 1.122 [bulk_mod] => 159.9 [shear_mod] => 54.8 [vicker_hard] => 8.2 [ref_file] => [publ_year] => [ref] => ) [1] => Array ( [id] => 386 [topology] => crb [link_rcsr] => [in_col] => 1 [transitivity] => [1232] [space_group] => I4/mmm [pearson] => tI24 [cn] => 2, 4 (2:1) [Year] => 2013 [cn_sort] => 002-004-002-001- [topology_str] => crb [sp_atoms] => + [caid] => 61 [nn] => 1 [name] => 1-Yne [pressure] => [density] => [e_gap] => 0.416 [energy] => [bulk_mod] => 69.8 [shear_mod] => [vicker_hard] => [ref_file] => /References/2013_SolidStateCommunications_169_50_56 [publ_year] => 2013 [ref] => ) )
SACADA Database Code: 61 Topology: crb (Allotrope with "sp" atoms) # of independent nodes (IN): 1 Transitivity: [1232] Space Group: I4/mmm Pearson: tI24 Coordination Number (CN): 2, 4 (2:1) Year: 2013 ![]() ![]() |
|
Name |
Pressure, GPa |
Density, g/cm³ |
Gap, eV |
Relative energy, eV/atom |
Bulk, GPa |
Shear, GPa |
Vickers, GPa |
Refs |
---|---|---|---|---|---|---|---|---|
crb (SACADA #61) | 1.911 | 1.122 | 159.9 | 54.8 | 8.2 | SACADA¹ | ||
1-Yne | 0.416 | 69.8 | doi: 10.1016/j.ssc.2013.07.001 ![]() |
4897.0931 | 1217.0727 | 200.2737 | 23.1387 | -37.3190 | -2.0385 |
1217.0727 | 4925.7871 | 149.8426 | 5.4763 | 49.8397 | 1.5029 |
200.2737 | 149.8426 | 2542.7157 | -7.6642 | -20.7080 | -0.0199 |
23.1387 | 5.4763 | -7.6642 | 228.7420 | 2.4528 | -3.4708 |
-37.3190 | 49.8397 | -20.7080 | 2.4528 | 153.4393 | -0.1503 |
-2.0385 | 1.5029 | -0.0199 | -3.4708 | -0.1503 | 155.4589 |