Array ( [0] => Array ( [id] => 847 [topology] => 3,4<sup>2</sup>T243 [link_rcsr] => [in_col] => 3 [transitivity] => [3983] [space_group] => P4/mcc [pearson] => tP48 [cn] => 3, 4 (1:2) [Year] => 2016 [cn_sort] => 003-004-001-002- [topology_str] => 3,4<sup>2</sup>T243 [caid] => 195 [nn] => 0 [name] => [pressure] => [density] => 2.488 [e_gap] => [energy] => 0.378 [bulk_mod] => 290.8 [shear_mod] => 163.2 [vicker_hard] => 19.7 [ref_file] => [publ_year] => [ref] => ) [1] => Array ( [id] => 848 [topology] => 3,4<sup>2</sup>T243 [link_rcsr] => [in_col] => 3 [transitivity] => [3983] [space_group] => P4/mcc [pearson] => tP48 [cn] => 3, 4 (1:2) [Year] => 2016 [cn_sort] => 003-004-001-002- [topology_str] => 3,4<sup>2</sup>T243 [caid] => 195 [nn] => 1 [name] => 4080-carbon [pressure] => [density] => 2.471 [e_gap] => Semimetal [energy] => [bulk_mod] => 292 [shear_mod] => 228 [vicker_hard] => 33 [ref_file] => /References/2016_AIP_advances_6_065225 [publ_year] => 2016 [ref] => ) )
SACADA Database Code: 195 Topology: 3,42T243 # of independent nodes (IN): 3 Transitivity: [3983] Space Group: P4/mcc Pearson: tP48 Coordination Number (CN): 3, 4 (1:2) Year: 2016 Download CIF File Download PDF report |
|
Name |
Pressure, GPa |
Density, g/cm³ |
Gap, eV |
Relative energy, eV/atom |
Bulk, GPa |
Shear, GPa |
Vickers, GPa |
Refs |
---|---|---|---|---|---|---|---|---|
3,42T243 (SACADA #195) | 2.488 | 0.378 | 290.8 | 163.2 | 19.7 | SACADA¹ | ||
4080-carbon | 2.471 | Semimetal | 292 | 228 | 33 | doi: 10.1063/1.4955055 |